Addition of 1% diluant to the readily prepared siliconemixture ( base + hardner ) decreases the Shorehardnes by 1 to 1.5 points.

Maximum addition : 10 % ( allows you to bring Shore from 25 (= strong rubber) to 10 ( = more flexible rubber ).

This means you no longer need different siliconerubbers with different Shorevalues . Just one with a relative high Shorevalue is enough; the diluant takes care of the lower shorevalues simply by adding it to the already mixed silicone-hardnermixture.

Addition of 1 - MAX 5% (by weight)  to the white base component BEFORE adding hardner.

Colour : pink.

High cure rates can be interesting when making dipmoulds or brushed-on moulds; it will allow you to built up several layers in a shorter period of time.

Mixtures containing accelerant can be further thickened with universal rubberthickener or thixothropic agent if desired and can be diluted with diluant for silicones to lower or adjust the final shore hardness.

Addition of a small amount of thix to a mixture of silicone + hardner will immediately thicken the mixture.

Degree of thickening can be choosen by adding more / less thix to the mixture.

Compared to the universal rubberthickener ( dusty powder ) this product will work much cleaner and faster but there is a tendency to a somewhat higher sheerweakness when using thix.

A flexibel and strong material, excellent to make masks and moulds of bas-reliefs and ornaments. To be apllied by means of a brush in several consecutive layers; can be thickened with our thickening agent for Latex.

No shrinkage is to be expected due to the prevulcanisation process applied to the product.

Dries to the air in one night ( when applied in a thin layer ) ; drying can be accelerated with a hairdryer or with a microwave oven at moderate power.

Latexmoulds can be reused up to  50 + times before rupture.

This product allows to thicken any kind of liquid moulding latex ( standard or pre-vulcanised ). Not to be used with silicones.

Allows to build up a brushed-on mould much faster and in less steps than normal.

Hairdryers or a microwave oven at moderate power can be used to speed up the drying.

This Epoxy varnish resin ( 2 componentsystem ) is very strong and completely clear .
Looks like molten glass.
To be used on tabletops, servingtrays, riverbeds in a modellandscape... or can be cast in larger thicknesses - up to 2 cm - as a less expensive replacement for the PUR Model 8 Transparant resin.
Can be coloured with pigments ( see our 'Pigments for castingresins' ).
Hardening in 12 hours. This set contains +- 0.9 liter of epoxyresin.
It has a slight tendency to yellow overtime when exposed to day- and sunlight.
For more info on how clear this resin is , click on ' click here for more product information'.

Component A for HARD POLYURETHANE CFK-FREE casting foam with a light beige colour.
Density : 75 kg/m³.
Mixing Ratio : 100 parts by weight A : 140 parts by weight B
Starttime : 70 seconden.
Very hard non-porous skin with closed cellstructure - thus waterrepellent.
Lightweight product for very detailed castings.
1 set ( 1 x Comp A H75-AT 0.7 kg + 1 x Comp B Type-2 1 kg ) gives you : 22.7 liter of foam.
Can be painted with all normal paintsystems after applying 1 layer of multiprimer first or can be coloured by adding a few drops of our pigments for casting resin just before mixing A and B.

THIS IS ONLY THE A COMPONENT / SEE OTHER ITEM FOR B COMPONENT !

Component A for HARD POLYURETHANE CFK-FREE casting foam with a light beige colour.
Density : 400 kg/m³.
Mixing Ratio : 100 parts by weight A : 100 parts by weight B
Starttime : 70 seconden.
Very hard non-porous skin with closed cellstructure - thus waterrepellent.
Lightweight product for very detailed castings.
1 set ( 1 x Comp A H400-AT 1 kg + 1 x Comp B Type-2 1 kg ) gives you : 5 liter of foam.
Can be painted with all normal paintsystems after applying 1 layer of multiprimer first or can be coloured by adding a few drops of our pigments for casting resin just before mixing A and B.

THIS IS ONLY THE A COMPONENT / SEE OTHER ITEM FOR B COMPONENT !

Component B for all HARD POLYURETHANE CFK-FREE casting foams ( H75-AT and 400-A ) 

THIS IS ONLY THE B COMPONENT / SEE OTHER ITEM FOR A COMPONENT !

Component A 0.740 kg + B 0.260 kg for FLEXIBLE POLYURETHANE CFK-FREE casting foam with a light beige colour.
Density : 60 kg/m³.
Mixing Ratio : 100 parts by weight A : 35 parts by weight B
Starttime : 70 seconden.
Very flexible non-porous skin with closed cellstructure - thus waterrepellent.
Lightweight product for very detailed castings.
1 set ( 1 x Comp A E-90 0.74 kg + 1 x Comp B E-90 0.26 kg ) gives you : 16 liter of flexible foam.
Can be coloured by adding a few drops of our pigments for casting resin just before mixing A and B.

Component A 1 kg + B 0.45 kg for FLEXIBLE POLYURETHANE CFK-FREE casting foam with a light beige colour.
Density : 200 kg/m³.
Mixing Ratio : 100 parts by weight A : 45 parts by weight B
Starttime : 70 seconden.
Very flexible non-porous skin with closed cellstructure - thus waterrepellent.
Lightweight product for very detailed castings.
1 set ( 1 x Comp A E-200 1 kg + 1 x Comp B E-200 0.45 kg ) gives you : 5 liter of flexible foam.
Can be coloured by adding a few drops of our pigments for casting resin just before mixing A and B.

Beachwooden mixing / stirring disposable woods

NOT AVAILABLE IN OTHER LANGUAGES ; DUTCH ONLY.

Uitgebreide NEDERLANDSTALIGE cursus maltechnieken die een overzicht biedt van de meest voorkomende maltechnieken , werkwijzen, produktbeschrijvingen en gebruiksaanwijzingen. Met veel tabelinformatie, fotomateriaal, stap voor stap toelichting.

Afleveringsvorm : A4 formaat, kleur, ingebonden met ringen OF CD-ROM met pdf bestand +- 9 MB

Niet verkrijgbaar in andere talen !

Druk op 'Klik Hier' voor enkele verkleinde afbeeldingen van pagina's in de cursus.